Abstract
A new low Ni maraging steel, based on 18Ni (300) type has been developed. The optimized chemical composition (complex alloyed with Al-Si-Ti or Si-Zr-Nb) in accordance with optimum heat treatment was found (solution: 970 °C/1h/air and ageing: 550 °C/3h/air), in order to obtain maximum service temperature of over 600 0C and ensured the good combination of strength and toughness properties. The precipitates, such as Ni3(Mo, Ti), were well controlled in lath martensite (Rm=2090N/mm2 and Rp0,2=1930N/mm2)and the presence of Si, Zr and Nb enhance structure stability at high temperature (for example the ultimate tensile strength at 5500C is about 1440N/mm2). Therefore, this new type of maraging steel was the subject of a national patent: “Maraging steel for high temperature service and heat treatment technology” – PATENT No.120356/30.08.2010.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.