Abstract
ABSTRACTHigh and very high cycle fatigue tests were performed to examine the microstructure and fracture mechanism of GH4169 superalloy in combination with techniques including electron‐backscatter diffraction (EBSD). Fractographic analysis revealed that surface failures are induced by surface flaws, whereas internal failures are caused by pores, facets, and inclusions. The three‐dimensional observation shows that fracture surfaces exhibit an irregular texture due to crystallographic mismatch of grains and plastic deformation at the crack tip. Based on EBSD analysis, Euler angles exhibited a complex geometry of grain orientation at the crack tip area, hindering crack propagation as evidenced by lower values of the Schmid factor and misorientation at the crack tip. Furthermore, the threshold values of small and long cracks decrease, whereas the transformation sizes from small to long crack growth increase from surface to internal failure. Finally, a novel microstructure defect‐based life prediction model is established, and the predicted results demonstrate a close resemblance to experimental outcomes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.