Abstract
Poly[(R)-3-hydroxybutyrate] (PHB) was blended with an aliphatic copolyester, which was synthesized by the esterification of adipic acid, ethylene glycol, and lactic acid. The blend showed a single T g , which varied systematically but convexly upwards with the composition. The growth rate of PHB spherulites, the crystallization temperature, and the equilibrium melting temperature of the blend were decreased as the amount of the copolyester was increased. Therefore, the blend system was determined to be compatible. However, the degree of crystallinity, and the enthalpies of crystallization and fusion of PHB in the blend remained almost constant, regardless of the compositional change, although the crystallization rate was decreased upon blending. No chemical change such as transesterification was observed as a result of the blending, yet there was a slight change in the crystalline morphology of PHB. The rate of fungal degradation was lowered with an increase in the copolyester content of the blend.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.