Laser-arc hybrid welding is prospectively considered as a high-efficiency and high-quality welding method for medium and thick section steels. SUS316L and XM-19 stainless steels are widely used in components and structures for nuclear power plants. This paper investigated the welding properties in Nd:YAG-GMAW hybrid welding of SUS316L and XM-19 stainless steels. With a hybrid welding system that was combined with a 4kW YAG laser and a 450A GMAW welder, 12mm thick SUS316L plates and 6mm thick XM-19 pipe was respectively bead-on-plate and butt-joint welded without backing plate. The effect of laser-to-arc distance (DLA) on the weld bead shape and porosity was discussed. The result shows that the DLA has significant influence on the stability of penetration and the formation of porosity for SUS316L, but has little influence for XM-19. Further analyses indicate that the high manganese content of XM-19 contributes to the welding process stability. Then the microstructures and mechanical properties of the hybrid-welded joint were also investigated.Laser-arc hybrid welding is prospectively considered as a high-efficiency and high-quality welding method for medium and thick section steels. SUS316L and XM-19 stainless steels are widely used in components and structures for nuclear power plants. This paper investigated the welding properties in Nd:YAG-GMAW hybrid welding of SUS316L and XM-19 stainless steels. With a hybrid welding system that was combined with a 4kW YAG laser and a 450A GMAW welder, 12mm thick SUS316L plates and 6mm thick XM-19 pipe was respectively bead-on-plate and butt-joint welded without backing plate. The effect of laser-to-arc distance (DLA) on the weld bead shape and porosity was discussed. The result shows that the DLA has significant influence on the stability of penetration and the formation of porosity for SUS316L, but has little influence for XM-19. Further analyses indicate that the high manganese content of XM-19 contributes to the welding process stability. Then the microstructures and mechanical properties of the hybri...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.