GdAlO3:Er3+/Yb3+, Gd3Al5O12:Er3+/Yb3+ and Gd4Al2O9:Er3+/Yb3+ phosphors were prepared by co-precipitation. The effects for Gd2O3-Al2O3 composite oxides as the host materials with different crystal structures such as GdAlO3, Gd3Al5O12 and Gd4Al2O9 were investigated. It was found that the perovskite structured GdAlO3:Er3+/Yb3+ (GAP phosphor) could be obtained from the precursor when the calcination temperature was 1000 °C, while the garnet structured Gd3Al5O12:Er3+/Yb3+ (GAG phosphor) could be formed when the calcination temperature was 1300 °C, but the monoclinic-structured Gd4Al2O9:Er3+/Yb3+ (GAM phosphor) could be formed only when the calcination temperature was raised up to 1500 °C. The difference of the up-conversion photoluminescence (UCPL) spectra under 980 nm between the GAP, GAG and GAM phosphors was studied. The result showed that the UCPL intensity of the GAP phosphor was close to that of the GAM phosphor with much higher red-to-green intensity ratio than that of GAP phosphor. The UCPL intensity of GAG phosphor was the weakest among them. Finally, the factors which influenced on the UCPL of the GAP, GAG and GAM phosphors were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.