Abstract
ObjectivesThe purpose of this study was to investigate the suitability of the Bend and Free Recovery (BFR) method as a standard test method to determine the transformation temperatures of heat-activated Ni-Ti orthodontic archwires. This was done by determining the transformation temperatures of two brands of heat-activated Ni-Ti orthodontic archwires using the both the BFR method and the standard method of Differential Scanning Calorimetry (DSC). The values obtained from the two methods were compared with each other and to the manufacturer-listed values. MethodsForty heat-activated Ni-Ti archwires from both Rocky Mountain Orthodontics (RMO) and Opal Orthodontics (Opal) were tested using BFR and DSC. Round (0.016 inches) and rectangular (0.019×0.025 inches) archwires from each manufacturer were tested. The austenite start temperatures (As) and austenite finish temperatures (Af) were recorded. ResultsFor four of the eight test groups, the BFR method resulted in lower standard deviations than the DSC method, and, overall, the average standard deviation for BFR testing was slightly lower than for DSC testing. Statistically significant differences were seen between the transformation temperatures obtained from the BFR and DSC test methods. However, the Af temperatures obtained from the two methods were remarkably similar with the mean differences ranging from 0.0 to 2.1°C: Af Opal round (BFR 26.7°C, DSC 27.6°C) and rectangular (BFR 27.6°C, DSC 28.6°C); Af RMO round (BFR 25.5°C, DSC 25.5°C) and rectangular (BFR 28.0°C, DSC 25.9°C). Significant differences were observed between the manufacturer-listed transformation temperatures and those obtained with BFR and DSC testing for both manufacturers. SignificanceThe results of this study suggest that the Bend and Free Recovery method is suitable as a standard method to evaluate the transformation temperatures of heat-activated Ni-Ti orthodontic archwires.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.