Abstract
ABSTRACT(0001) aluminium nitride thin films were grown epitaxially on (0001) Sapphire substrates by MOCVD at 1200° C and PLD at 800° C. Both films have the same epitaxial growth relationship: (0001)AlN//(0001)Sap, and the same in-plane relationship which shows a 30° rotation between A1N and Sapphire: [ 12 10]AlN//[0 110]Sap and [10 10]AlN //[ 2110]Sap. The full width at half maximum (FWHM) of x-ray rocking curve of the MOCVD A1N film was 0.16° and PLD A1N film was 0.2°. Films grown by both MOCVD and PLD showed high crystalline quality. HRTEM images showed that these films are single crystalline with very low density of defects.Dislocations in the film parallel to the film / substrate interface were observed in both A1N films. Atomic force microscopy images showed that the MOCVD films have flatter and larger terraces than the PLD films. The PLD technique for A1N growth needs to be improved further. But both films have a surface roughness of approximately 100nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.