Abstract
We investigated the influence of a fuel change from pure hydrogen to a hydrogen–ammonia mixture at different percentages on the electrochemical behavior of 50 mm in diameter Solid Oxide Fuel Cells (SOFCs) with sputtered thin buffer layers of Gd-doped ceria, varying the working temperatures from 800 °C to 650 °C. The results show that the performances of the cells are not affected by the fuel change for high working temperatures (800 °C and 750 °C). As an example, a power density value of 802 mW∙cm−2 at 1 A∙cm−2 is found when directly feeding the cell with 8 NmL∙min−1cm−2 of ammonia and with an equivalent flowrate of 12 NmL∙min−1cm−2 of H2. These power density output values are higher than those obtained in industrial state-of-art (SoA) SOFCs with screen-printed buffer layers fed with equivalent hydrogen flowrates, thanks to the improved electrochemical performances obtained in the case of cells with sputtered thin buffer layers of Gd-doped ceria. At lower working temperatures (700 °C and 650 °C), slight changes in the electrochemical behavior of the cells are observed. Nevertheless, in this temperature range, we also obtain an output current density value of 0.54 A∙cm−2 in a pure ammonia flowrate of 12 NmL min−1cm−2 at 800 mV and 700 °C, equal to the value observed in SoA button cells with industrial screen-printed GDC barrier layer fueled with 16 NmL∙min−1cm−2 of H2. These results pave the way towards the use of innovative SOFC structures with sputtered thin buffer layers fueled by ammonia.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have