Abstract
A systematic study of the gamma irradiation effects on single wall carbon nanotube (SWCNT) structure was conducted. Nanotubes were exposed to different doses of gamma irradiation in three media. Irradiation was carried out in air, water and aqueous ammonia. Thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), elemental analysis (EA) and Raman spectroscopy confirmed the changes in the SWCNT structure. TGA measurements showed the highest percentage of introduced groups for the SWCNTs irradiated with 100 kGy. FTIR spectroscopy provided evidence for the attachment of hydroxyl, carboxyl and nitrile functional groups to the SWCNT sidewalls. Those groups were confirmed by EA. All irradiated SWCNTs had hydroxyl and carboxyl groups irrelevant to media used for irradiation, but nitrile functional groups were only identified in SWCNTs irradiated in aqueous ammonia. Raman spectroscopy indicated that the degree of disorder in the carbon nanotube structure correlates with the irradiation dose. For the nanotubes irradiated with the dose of 100 kGy, the Raman I{sub D}/I{sub G} ratio was three times higher than for the pristine ones. Atomic force microscopy showed a 50% decrease in nanotube length at a radiation dose of 100 kGy. Scanning and transmission electron microscopies showed significant changes in the morphology and structuremore » of gamma irradiated SWCNTs. - Highlights: Black-Right-Pointing-Pointer Gamma irradiation causes SWCNT covalent functionalization. Black-Right-Pointing-Pointer Type of covalently attached groups to SWCNT surface depends on irradiation medium. Black-Right-Pointing-Pointer The SWCNT shortening level increases with applied irradiation dose. Black-Right-Pointing-Pointer The average length of carbon nanotubes decreased by 50% at the highest dose. Black-Right-Pointing-Pointer The diameter of SWCNT bundles becomes small as irradiation dose rises.« less
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have