Abstract
Background and aims. Present study was designed to compare the bonding strength of resin-modified glass ionomer (RMGI) and composite resin to mineral trioxide aggregate (MTA), MTA mixed with Na2HPO4 (NAMTA), and calcium-enriched mixture (CEM). Materials and methods. Thirty specimens of each CEM, NAMTA, and MTA were prepared. Composite and RMGI restorations were then placed on the samples (15 samples in six subgroups). Shear bond strength was assessed using universal testing machine. Data were analyzed with two-way ANOVA and post-hoc Tukey test. To compare the bond strength in subgroups, one-away ANOVA was applied. Significance level was set at P < 0.05. Results. Bond strength was significantly higher to composite samples compared to RMGI samples (p<0.001). The difference in bond strength of composite samples between MTA and CEM subgroups (P=0.026) as well as MTA and NAMTA subgroups (P= 0.019) was significant, but the difference between NAMTA and CEM subgroups (P=0.56) was not significant. The differences in bond strength in subgroups of RMGI group were not significant (P>0.05). Conclusion. Regarding shear bond strength to the tested substrates, composite was shown to be superior to RMGI. The bond of resin composite to MTA was weaker than that to CEM and NAMTA.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Dental Research, Dental Clinics, Dental Prospects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.