Abstract
Abstract The paper presents results of the research which aim was to compare the corrosion resistance of alloys based on intermetallic phase after Fe40Al5CrTiB crystallization and after forming the steel corrosion resistant X12CrCoNi2120 species. The tests were performed for steel at temperature of 700°C Fe40Al5CrTiB and for alloy at 1100°C and 9% O2 0.2% HCl + SO2+ 0.08 N2 environment. In the research the changes of weight after corrosion tests, observations of the surface, specified chemical and phase composition of corrosion products were made. The obtained results of the study showed a very good corrosion resistance of Fe40Al5CrTiB alloys in high temperature and environments containing oxygen, sulfur and chlorine as compared to the corrosion resistance of the steel grade X12CrCoNi2120. Results of the research conducted in this scope are the basis for further research.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.