Abstract
The heat treatment response of semisolid metal high pressure die cast Al–7Si–Mg alloys A356 and F357 was studied and compared. It was found that the heat treatment behaviour of alloy F357 is influenced markedly by the stability of the Mg containing π phase. This phase, which dissolves in alloy A356 during solution treatment, persists in F357 and decreases the amount of magnesium in solid solution. This is the likely origin of the decrease in the aging response of the F357 alloy. The tensile properties (yield strength and ultimate tensile strength) of the alloys correlate much better with the Mg concentration in solid solution than with the bulk Mg content of the alloys. The recently developed shortened T6 heat treatment cycles for rheocast A356 were tested on alloy F357. The optimum artificial aging treatment was determined to be 180°C for 4 h, regardless of the prior natural aging period.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.