Abstract
This paper investigates the electrical activation of boron halide molecular implants into silicon and compares them to boron implants at the same effective energy. The implanted species: B+, BF2+, BCl2+ and BBr2+ were implanted to doses of 2×1014 and 1×1015Bcm−2 the energy of the molecular implants was calculated to give an effective boron implant energy of 5keV. Samples cut from the wafers were annealed for 30s at temperatures ranging from 800°C to 1100°C. Hall effect measurements were used to compare and contrast the electrical activation of the boron between the different halide species and doses. It was found that molecular implants of BBr2+ and BCl2+ do not enhance the electrical activation of boron to the same extent that BF2+ implants do. The BBr2+ implants are only comparable with boron after annealing at high temperatures (above 1000°C). The BF2+ implants show enhanced electrical activation with respect to boron for all the annealing temperatures and doses studied.Rutherford backscattering spectroscopy (RBS) of silicon implanted with BBr2+ to a dose of 1×1015boron atomscm−2, shows that an amorphous region is created during the implantation. This region fully re-grows after annealing at 1100°C; lower temperature anneals remove only part of the amorphous layer. RBS channelling shows that a fraction of the bromine takes up substitutional lattice sites upon implantation, and that this fraction increases as the samples are annealed at temperatures above 600°C with 40% of the B being in substitutional sites after annealing at 1050°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.