Abstract
Aluminum matrix composites reinforced by Al62Cu26Fe12 gas atomized powders were produced by conventional metallurgical processes, such as gravity casting with stirring and hot extrusion. This investigation was mainly focused on the dependency of the yield stress at room temperature as a function of the volume fraction of reinforcement, but other variables such as the matrix, coating layer around the particles, and processing were also investigated. For as-extruded composites, the addition of the Al-Cu-Fe particles improved the yield stress, although not dramatically owing to the large particle size. In contrast, it was found that the yield stress was considerably enhanced for the as-cast composites up to 10%(AlCuFe)p, while an asymptotic value was observed afterward. The dominant parameter appeared to be the strength of the matrix, which was found to be proportional to the volume fraction of the reinforcement. These results are discussed in relation with the possible strengthening mechanisms in order to estimate the role of the icosahedral and related crystalline phases on the increase of yield stress.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.