Abstract
Boron (B) removal by slag refining using CaO–SiO2–CaCl2 was investigated in metallurgical-grade silicon (MG-Si) and 75 wt% Si–Sn alloy. Experiments were conducted at 1500 °C for 15 min. The microstructure was characterized before and after refining. The effects of acid leaching, basicity, and slag/Si mass ratio on B removal were investigated. Experimental results showed that acid leaching had no effect on B removal from MG-Si but had a clear effect on the refined Si–Sn alloy after slag refining. The final B concentration was highly affected by the CaO/SiO2 mass ratio with minimum value, where the content of B was reduced from 18.36 ppmw to 5.5 ppmw at the CaO/SiO2 = 1.2 for MG-Si slag refining and from 18.36 ppmw to 3.7 ppmw at CaO/SiO2 = 1.5 for 75 wt% Si–Sn alloy. Increasing the slag mass ratio by 2:1 mass ratio also increased B removal efficiency by approximately 15–20% more than an increase by 1:1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.