Abstract
Three kinds of specimens were produced from hot strips of similar composition and same thickness (nominal gauge 4.0 mm) but produced using different technologies, and the dislocation density of these strips was quantitatively measured by positron annihilation technique test. The dislocation morphology and evolution in microstructure of each pass for producing the 1.9 mm hot strip using CSP (compact strip production) technology were observed under an H-800 transmission electron microscope; its density was also quantitatively measured using the positron annihilation technique test, and the factors influencing the dislocation density during the production process were analyzed. The experimental results show that the dislocation density in the microstructure produced using CSP technology is higher than that in the microstructure produced using conventional technology. This result was discussed and confirmed on the basis of the finite element simulation and the theory relevant to dislocations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of University of Science and Technology Beijing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.