Comparing Resilient Modulus and Dynamic Modulus of Hot-Mix Asphalt as Material Properties for Flexible Pavement Design

Abstract

With the current trend toward developing mechanistic flexible pavement design and the need for more reliable design procedures, accurate characterization of hot-mix asphalt (HMA) properties is needed. Resilient and dynamic modulus tests were performed at five temperatures on two typical mixes used in the Commonwealth of Virginia to compare the test results. The dynamic modulus was measured at six frequencies at each of the testing temperatures, and the resilient modulus test was performed at one loading time. The study found that the size of the specimen statistically affected the measured resilient modulus value. Resilient modulus values obtained in the 100-mm-diameter specimens were higher than those obtained in the 150-mm-diameter specimens at all testing temperatures. No statistical differences were observed in the resilient modulus of the two mixes. However, statistical differences were found in the dynamic modulus of the two mixes. A strong relation between the dynamic modulus test performed at 5 Hz...