Abstract
The dry sliding wear behavior of MoS2 and WS2 was studied with plasma-nitrided SG iron. Both the lubricants were effective in preventing wear loss of the sliding material due to low friction. The specific wear rate of coated material was 10 times lower than uncoated material. The coefficient of friction of MoS2 and WS2 was 0.1 and 0.03, respectively. Wear damage was observed to be significantly lower for lubricant-coated material compared to uncoated part.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.