Two kinds of segmentation-crack structured YSZ thick thermal barrier coatings (TTBCs) were deposited by suspension plasma spraying (SPS) and atmospheric plasma spraying (APS) with nano-based suspension and agglomerated particles, respectively. The phase composition, microstructure evolution and failure behavior of both TBCs before and after thermal shock tests were systematically investigated. Microstructure of the APS coating exhibits typical segmentation-crack structure in the through-thickness direction, similar with the SPS coating. The densities of segmentation-crack in APS and SPS coatings were about 3 cracks mm−1 and 4 cracks mm−1, respectively. The microstructure observation also showed that the columnar and equiaxed grains existed in the SPS coating. As for the thermal shock test, the spallation life of the APS TTBCs was 146 cycles, close to that of the SPS TTBCs (166 cycles). Failure of the APS coating is due to the spallation of fringe segments and splats.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.