Abstract
Various electrochemical techniques were used to study the corrosion behaviour of the CNT-reinforced NiAl alloys under NaCl and Na2SO4 environments. The potentiodynamic polarization curves revealed activation Tafel behaviour when the NiAl alloy specimens were immersed in NaCl solution while passivation followed by slight development of transpassivation resulted under Na2SO4 environment. The reinforcement of pure NiAl alloy with up to 1.0 wt.% CNT increased the corrosion rate from 0.10 to 0.63 mm/yr under NaCl environment, while under Na2SO4 environment, the corrosion rate increased from 0.04 to 0.12 mm/yr. The observed increase in corrosion rate with an increase in CNT reinforcement (under both NaCl and Na2SO4 environments) suggested that the reinforcement of NiAl alloys with CNT reduced the corrosion resistance of NiAl. The X-ray diffraction analysis revealed that the corrosion products consisted of oxides including Al2O3 under NaCl environment, while scanning electron microscope analysis showed a porous passive layer on the surface of the alloy specimens immersed in Na2SO4 solution.Graphical abstract
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.