Abstract
The Er3+/Yb3+doped La2O3 phosphor samples were synthesized by the combustion method and then photoluminescence and photoacoustic spectroscopic studies were done. Prepared samples were annealed at 800 °C, 1000 °C and 1300 °C and all samples were found in pure hexagonal phase as confirmed by XRD analysis. From FE-SEM images it is found that particle size increases with increase in annealing temperature. The frequency upconversion emission spectra of samples were recorded by exciting the sample with 980 nm diode laser and maximum emission intensity is obtained for the sample annealed at 1000 °C for 2 h. A photoacoustic cell was designed and wavelength dependent photoacoustic spectra were measured. The effect of sample storage time on radiative and non-radiative emission properties of sample was checked by measuring upconversion emission and photoacoustic spectra, simultaneously. It is observed that the emission intensity and photoacoustic signal both decreases with time. The maximum photoacoustic signal is obtained around 974 nm wavelength and it indicates its potential for photo-thermal therapy using infrared excitation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.