Abstract
The effect of the addition of 0.1 wt% Sc and 0.1 wt% Er on the deformation microstructure, Vickers microhardness, and electrical conductivity of Al-0.2 wt% Zr-based alloy cables annealed at 400 °C for different times was investigated. The comprehensive properties of Al-0.2Zr-0.1Sc were better than those of Al-0.2Zr-0.1Er. The optimal conditions for the Al-0.2Zr-01Sc alloy cable were a microhardness of 575 MPa, an electrical conductivity of 34.5 MS/m for an annealing time of 36 h, and those for the Al-0.2Zr-0.1Er alloy cable were a microhardness of 550 MPa, an electrical conductivity of 33.6 MS/m for an annealing time of 8 h. During the annealing process, dispersed Al3(Zr,Sc/Er) precipitates were generated, which substantially impeded recrystallization by Zener pining of grain boundaries. Based on the ratio of volume fraction (FV) to average diameter (d¯) of the precipitates, their capability to inhibit recrystallization was as follows: Al3(Zr, Sc) > Al3(Zr, Er) > Al3Zr. Moreover, the electrical conductivity of Al-0.2Zr-0.1Sc was better than that of Al-0.2Zr-0.1Er, probably because Sc could better inhibit recrystallization than Er, leading to fewer grain boundaries and hence lesser electron scattering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.