Abstract
High-performance thin films combining large optical bandgap Al2O3 and high refractive index HfO2 are excellent components for constructing the next generation of laser systems with enhanced output power. However, the growth of low-defect plasma-enhanced-atomic-layer-deposited (PEALD) Al2O3 for high-power laser applications and its combination with HfO2 and SiO2 materials commonly used in high-power laser thin films still face challenges, such as how to minimize defects, especially interface defects. In this work, substrate-layer interface defects in Al2O3 single-layer thin films, layer-layer interface defects in Al2O3-based bilayer and trilayer thin films, and their effects on the laser-induced damage threshold (LIDT) were investigated via capacitance-voltage (C-V) measurements. The experimental results show that by optimizing the deposition parameters, specifically the deposition temperature, precursor exposure time, and plasma oxygen exposure time, Al2O3 thin films with low defect density and high LIDT can be obtained. Two trilayer anti-reflection (AR) thin film structures, Al2O3/HfO2/SiO2 and HfO2/Al2O3/SiO2, were then prepared and compared. The trilayer AR thin film with Al2O3/HfO2/SiO2 structure exhibits a lower interface defect density, better interface bonding performance, and an increase in LIDT by approximately 2.8 times. We believe these results provide guidance for the control of interface defects and the design of thin film structures and will benefit many thin film optics for laser applications.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.