Abstract
Abstract In order to study the effect of sintering temperature and A-site cation radius on the structural, magnetic and transport properties, a systematic investigation of La0.5Nd0.2Ca0.3–xKxMnO3 (x = 0.0 and 0.05) nanoparticles has been undertaken. Rietveld analysis of X-ray diffraction data confirmed the presence of orthorhombic symmetry with Pbnm space group for all the samples. A paramagnetic-ferromagnetic transition is shown by all our investigated compounds. The materials exhibit semiconducting behavior and the metal-semiconductor transition temperatures (TMS) are found to be close to Curie temperatures (Tc), indicating a strong correlation between their electrical and magnetic properties. Both Tc and TMS of K-doped samples were found to be higher than their undoped counterparts at same calcination temperatures. In the high temperature region, it was observed that the resistivity data was best fitted by SPH model.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.