Abstract
In this study, the film forming behaviour of low amylose (LA) and high amylose (HA) starches was studied. The starch-alone and a blend of plasticizer (polyol)–starch films were developed by gelatinising at various temperatures and casting at 25°C. The starch–plasticizer films contained glycerol and xylitol either individually or in 1:1 combination. The concentration of plasticizer used was 15%, 20% and 30% for LA films while it was 20%, 30% and 40% for HA films on dry solid basis. The HA-glycerol films retained the highest moisture content among all the films. The HA films exhibited higher glass transition temperature, higher tensile strength, higher modulus of elasticity and lower elongation at break than those obtained from LA starch. The tensile strength and modulus of elasticity decreased and the elongation increased with increasing plasticizer concentrations above 15% on dry solid basis regardless the starch type. Low water vapour permeability was evident in LA and HA films plasticized by combined plasticizers at 20% plasticizer concentration. Rheological measurements showed that most of the suspensions exhibited Herschel–Bulkley behaviour and some of the HA suspensions exhibited Bingham plastic behaviour. At 15% (on dry solid basis) plasticizer concentration, the films obtained from both the starches were brittle due to the anti-plasticization behaviour.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.