Comparative performance of various smart aggregates during strength gain and damage states of concrete

Abstract

Information regarding the early strength gain of fresh concrete determines the time for the removal of form work and the transfer of pre-stressing forces for pre-stressed concrete. An ultrasonic based non-destructive evaluation of early strength gain may not work for concrete in fluid and semi-solid phases. A possible alternative is a lead zirconate titanate (PZT)-based smart aggregate embedded in concrete, which can evaluate the micro-structural and rheological properties right from the fluid phase. A set of five smart aggregates embedded in a concrete cube were investigated for their suitability to evaluate electromechanical impedance (EMI) signatures. Cubes were loaded to failure and the EMI during progressive strength loss under compressive loads was studied. To show the generalized applicability of this, experimental results for the performance of typical smart aggregates on a larger specimen, namely a concrete beam, are also discussed. Different statistical metrics were examined computationally on a three peak admittance curve with a parametric variation of stiffness, damping and simple scaling. The root mean square deviation (RMSD), mean absolute percentage deviation (MAPD), cross correlation (CC) and modified cross correlation (MCC) were investigated, in addition to the rate of change of the RMSD. Variations between the reference and modified states were studied. Both stiffness and mass gains occur for the smart aggregates, resulting in an increase or decrease of frequency and amplitude peaks due to progressive C-S-H gel formation. The trend of increasing stiffness and the consequent rightward shift of the resonant peaks and decrease of damping, with the consequent upward shift of amplitudes that happens during curing and strength gain, was observed to be reversed during the application of damaging loads.