Abstract
Objective: The aim of this in vitro study was to evaluate the bond strength of a new calcium silicate cement, Neo MTA Plus (Avalon Biomed Inc. Bradenton, FL, U.S.A) by comparing ProRoot MTA and Biodentine.Material and Methods: Sixty dentin slices were instrumented to achieve a diameter of 1.3 mm. Group 1: white ProRoot MTA, group 2: Biodentine, group 3: Neo MTA Plus – G (powder mixed with gel), group 4: Neo MTA Plus – W (powder mixed with distilled water) were loaded into cavities. The push-out bond strength values were measured. Data were analyzed using Welch ANOVA with Bonferroni correction p = 0.05. Failure modes (adhesive, cohesive, and mixture) were analyzed.Results: The highest bond strength value was recorded in Neo MTA Plus mixed with gel (5.23 ± 1.78 MPa), whereas white ProRoot MTA (2.57 ± 0.66 MPa) had the lowest. Bond strength values of Neo MTA Plus mixed either with gel or with distilled water were statistically different from both white ProRoot MTA and Biodentine (2.61 ± 0.70 MPa) (p < 0.05). Adhesive failure was predominantly observed in all groups.Conclusion: Neo MTA Plus could be considered as alternatives to the ProRoot MTA and Biodentine due to its better performance in bonding to root dentin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.