Abstract
Aim:The study was done to evaluate the fracture resistance of carbon, glass fiber, and zirconia posts.Materials and Methods:Forty-five human premolars indicated for orthodontic extraction were subjected to root canal treatment and obturated with gutta-percha. All the teeth were decoronated and mounted in acrylic block. Then, teeth were equally divided into three groups: (a) carbon, (b) glass fiber, and (c) zirconia post group. Post space was prepared and particular post was cemented in post space. Core buildup was made with composite. A compressive load was applied using universal testing machine and fracture force was measured in MPa. The data were tabulated, and statistical evaluation was done using statistical software IBM SPSS Statistics for Windows, version 21.0., IBM Corp., Armonk, NY, USA, using one-way analysis of variance for analysis of difference and Bonferroni post hoc test.Results:Zirconia endodontic post had good fracture resistance (489.2 MPa) when compared with carbon (258.4 MPa) and glass fiber-reinforced post (348.7 MPa). Fracture resistance was statistically significant between test groups P>0.001.Conclusion:The present study concluded that zirconia had good fracture resistance compared to glass fiber and carbon posts.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of International Society of Preventive and Community Dentistry
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.