Comparative analysis of wear behavior of garnet and fly ash reinforced Al7075 hybrid composite

Abstract

AbstractAl7075 hybrid composites reinforced with varying weight percentage (0 wt.%, 5 wt.%, 10 wt.%, 15 wt.%) of each of garnet and fly ash were fabricated and characterized for their comparative wear assessment. The sliding wear test was conducted on a reciprocating tribometer in dry medium under the working conditions of applied normal load (2 N, 4 N, 6 N, 8 N), sliding velocities (0.04 m/s, 0.08 m/s, 0.12 m/s, 0.16 m/s), sliding distance (20 m, 40 m, 60 m, 80 m) and working temperature (25 °C, 50 °C, 75 °C, 100 °C). The experiments were performed as per steady‐state condition and Taguchi (L25) orthogonal array design to evaluate specific wear rate of the Al7075 hybrid composites. The finding of results indicated that the wear rate was decreased with the increase in the filler content in both the case of garnet and fly ash reinforced Al7075 hybrid composites. The results from Taguchi experiments suggested that the filler content and load were the most significant factors affecting wear behavior of composites while temperature and sliding distance are the least significant factors. Also, the garnet reinforced Al7075 hybrid composite indicated less specific wear rate as compared to that of fly ash reinforced Al7075 hybrid composite.