Abstract
Al-Si wrought piston alloys can lack properties due to inefficient grain refining. A novel Al-Nb-B grain refiner was introduced some time ago, but has still not been assessed in industry for wrought alloys. This paper describes the first trial of Al-Ni-B addition and its impact on the full-scale manufacturing, structure, and properties of the AA4032 products extruded with and without billet homogenization. It is shown that Nb-B inoculation gives opportunities not only to have a refined as-cast structure but also a more homogenous distribution of the solute. In contrast, homogenization drives nucleation and coarsening of the Mg2Si phase that is retained during further extrusion and heat treatment also affecting the precipitation and properties. It was observed that non-homogenized specimens perform better during machining and tensile testing compared to homogenized specimens. The results are supported by electron microscopy investigations of microstructure formation during different steps in downstream processing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.