Abstract
The CeO2 nano-particles dispersed on the surface of commercial LiNi0.5Co0.2Mn0.3O2, have been prepared by a co-precipitation method, in which ammonium carbonate or ammonium oxalate is served as a precipitant to generate the different precursor of CeO2, respectively. CeO2-modified LiNi0.5Co0.2Mn0.3O2 composites with ammonium oxalate as the precipitant exhibit the best electrochemical properties with a reversible lithium storage capacity of 157.7 mAh g−1 with a retention of 86.36% at 25 °C at the current density 1C after 100 cycles under high cut-off voltage 4.6 V. At higher temperature 55 °C, its discharge capacity changes from 198.2 mAh g−1 to 136.6 mAh g−1 after 100 cycles, with a retention of 68.29%. Besides, it also displays an excellent rate performance with a capacity of 114.0 mAh g−1 at 5C in the 100th cycle. All enhanced performances could be due to the dispersion of CeO2 on the surface of commercial LiNi0.5Co0.2Mn0.3O2 and the synergistic effects between the CeO2 and LiNi0.5Co0.2Mn0.3O2, which leads to the enhanced structural stability and electric conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.