Abstract
Solar selective paints, with the addition of Co3O4 as a pigment, are used to improve energetic efficiency in solar collectors. Although Co3O4has been obtained by different methods, references about combustion synthesis are scarce. Co3O4 powders have been synthesized by stoichiometric and non-stoichiometric routes using aspartic acid (Asp) or tri-hydroxi-methyl-aminomethane (Tris) as fuels. The samples were calcined in air at 500°C. They were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetric analysis, differential scanning calorimetry, Fourier transform infrared spectrum and the specific surface area of the samples was determined by means of the Brunauer–Emmett–Teller technique. The optical properties of pigments were assessed by means of a spectrophotometer. In all cases, powders exhibited the crystalline structure of Co3O4. A minimum crystallite average size of 29nm was observed for powders obtained by the “stoichiometric/Asp” combustion route, while a maximum value of 41nm was stated for powders obtained by the “non-stoichiometric/Asp” combustion process. The average particle size ranged between 50 and 100nm. The powders obtained by the“stoichiometric/Asp” method were selected to study their optical properties; their solar absorption value was 86%. Solar selective surfaces composed by Co3O4 pigments and an alkyd resin were obtained and applied over copper or aluminum substrates. In both cases, solar absorptance was of 93% and comparable with similar solar selective surfaces, but the thermal emittance value was higher than 90%, as a consequence of the large width of the films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.