Abstract
AbstractComposites of NbC/ZrO2 reinforced with different weight ratios of Cr metal were prepared by dynamic compaction combustion from a blend of Nb2O5–Zr–Cr powders. Factors controlling the synthesis process, the microstructure, and the mechanical properties of the samples, such as Cr wt% and the compression loads were studied. The samples were characterized by XRD, SEM, porosity, and hardness measurements. The porosity value of the sample with no additives was high and reached 31.6 vol%. A sudden decrease in the sample porosity to 2.4 vol % was noticed for the sample containing 3.0 wt% of Cr. A high‐density sample with less than 2.0 vol % porosity and maximum hardness of 1038 HV was produced using 5.0 wt% Cr under 300 MPa compression load. Detailed thermodynamic calculations for the effect of Cr additives on the physicochemical properties of the system were introduced.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.