Abstract
Concrete specimens with three types of cement (sulfate resistant high early strength – reference, pozzolanic, and with ground granulated blast furnace slag) reinforced with two types of steel (galvanized and carbon steel) were subjected to cycles of immersion in 1.0 M NaCl solution and drying at 40ºC. For each different steel-concrete condition, 6 rebars were tested. Experimental results show that galvanized steel presents longer corrosion initiation periods in concretes with supplementary cementitious materials. Particularly for pozzolanic concrete, this increased initiation period was 4.6 times longer on average, which reflects, in a similar way, on service-life simulations. In general, the average chloride thresholds of galvanized steel increased with a decrease in pore solution alkalinity. Compared to carbon steel, higher chloride thresholds were found for galvanized steel embedded in the lower alkalinity concrete matrix (calculated pore pH = 12.6). On the other hand, galvanized steel presented lower chloride thresholds for more alkaline pore pHs (pozzolanic and reference concretes).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.