Abstract
In this study, InP(1 0 0) surfaces were bombarded by argon ions in ultra high vacuum. Indium metallic droplets were created in well controlled quantities and played the role of precursors for the nitridation process. A glow discharge cell was used to produce a continuous plasma with a majority of N atomic species. X-ray photoelectron spectroscopy (XPS) studies indicated that the nitrogen combined with indium surface atoms to create InN thin films (two monolayers) on an In rich-InP(1 0 0) surface. This process occurred at low temperature: 250 °C. Synchrotron radiation photoemission (SR-XPS) studies of the valence band spectra, LEED and EELS measurements show an evolution of surface species and the effect of a 450 °C annealing of the InN/InP structures. The results reveal that annealing allows the crystallization of the thin InN layers, while the LEED pattern shows a (4 × 1) reconstruction. As a consequence, InN related structures in EELS and valence bands spectra are different before and after the annealing. According to SR-XPS measurements, the Fermi level is found to be pinned at 1.6 eV above the valence band maximum (VBM).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.