Colour agreement between try-in paste and resin cement: effect of background on zirconia-reinforced lithium silicate.

Abstract

To investigate colour agreement between different shades of Panavia V5 resin cement and their try-in pastes under zirconia-reinforced lithium silicate ceramics. Forty-four zirconia-reinforced lithium silicate ceramic specimens were prepared at 0.8 ± 0.01 mm thickness. Composite resin tooth-shaded background specimens were obtained in two shades. Resin cement specimens were fabricated at 0.1-mm thickness. Colour difference values (ΔE) between Aquagel and both the try-in paste and resin cement were calculated using the CIE-Lab system. The CIEDE2000 (ΔE00) colour formula was used to determine colour differences. The three-way ANOVA test and a multiple comparisons test were used for statistical analysis (α = 0.05). A statistically significant difference was found between the ΔE00 values obtained from the cement shade colour measurements for all specimens (P < 0.05). According to the three-way ANOVA test, lower ΔE00 values were observed in the try-in paste group compared to the resin cement group. The ΔE00 values were significantly affected by the cement shade and tooth-shaded background (P < 0.05). The colour agreement between the try-in pastes and the corresponding resin cement differed, and the try-in pastes could not mask the dark dental background as much as the corresponding resin cement.