Abstract
In the present work, polycrystalline Sm0.55Sr0.45MnO3 thin films were prepared on LSAT (001) single crystal substrates by ultrasonic nebulized spray pyrolysis technique. The X-ray diffraction θ-2θ scan reveals that these films (i) have very good crystallinity, (ii) are oriented along out-of-plane c-direction, and (iii) are under small tensile strain. The impact of oxygen vacancy results into (i) higher value of paramagnetic insulator (PMI) to ferromagnetic metal (FMM) transition temperature, i.e., TC/TIM, (ii) sharper PMI-FMM transition, (iii) higher value of magnetization and magnetic saturation moment, and (iv) higher value of magnetoresistance (∼99%). We suggest here that oxygen vacancy favors FMM phase while oxygen vacancy annihilation leads to antiferromagnetic-charge ordered insulator (AFM-COI) phase. The observed results have been explained in context of phase separation (PS) caused by different fractions of the competing FMM and AFM-COI phases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.