Abstract
Colloidal porous AuAg alloyed nanoparticles (pAuAgNPs) were synthesized by galvanic replacement reaction from Ag nanocubes. pAuAgNPs have a 50 nm exterior diameter and half of their inner space consists of voids that have a bimodal size distribution with peaks at 21 and 8.3 nm. pAuAgNPs showed a plasmonic peak at 750 nm, which was exploited for photoacoustic (PA) imaging. Gold nanorods (AuNRs) were prepared and used as the control; they have a strong plasmonic peak at 720 nm. In in vitro experiments at respective plasmonic peak excitations, pAuAgNPs gave stronger PA signals than AuNRs by 8.9 times per particle and 11.7 times per dosage by exogenous atom. The high surface area per volume as a result of the inner voids amplified the PA signals by efficient thermoacoustic conversion. In experiments of chicken-tissue phantoms, pAuAgNPs showed PA signals through 4.5 cm thick tissue, whereas AuNRs gave no detectable signal. In whole-body in vivo experiments, pAuAgNPs injected into the body showed 2.7 times stronger PA signals than AuNRs. Coating the pAuAgNPs with a silica layer additionally increased their PA signal by 1.8 times when compared to the uncoated ones.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.