Abstract
In this work, colloidal silicalite-1 single crystals are for the first time synthesized using fluoride as mineralizing agent at near neutral pH. SEM, TEM, DLS, XRD, solid-state (29)Si MAS NMR, and adsorption/desorption experiments using nitrogen, water, n-butanol, and ethanol as adsorbates were used to characterize the crystals. The single crystals have a platelike habit with a length of less than 170 nm and an aspect ratio (length/width) of about 1.2, and the thickness of the crystals is less than 40 nm. Compared with silicalite-1 crystals grown using hydroxide as mineralizing agent, the amount of structural defects in the lattice is significantly reduced and the hydrophobicity is increased. Membrane separation and adsorption results show that the synthesized defect-free crystals present high selectivity to alcohols from alcohol/water mixtures. The n-butanol/water adsorption selectivities were ca. 165 and 14 for the defect-free crystals and a reference sample containing defects, respectively, illustrating the improvement in n-butanol/water selectivity by eliminating the polar silanol defects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.