Abstract
Previous reports have shown that colloidal crystal (CC) films with visible Bragg reflection characteristics can be fabricated by the surface modification of monodisperse silica particles (SiPs) with poly(methyl methacrylate) (PMMA) chains, followed by hot-pressing at 150 °C. However, the reflection bands of the CC films were very broad due to their relative disordering of SiPs. In this report, we attempted to fabricate the CC films using SiPs surface-modified with poly(n-octyl acrylate) (POA) chains by hot-pressing. When the cast films of POA-grafted SiPs were prepared by hot-pressing at 100 °C, the reflection bands were narrow rather than those of CC films of PMMA-grafted SiPs. This can be ascribed to easy disentanglement of POA chains during the hot-pressing process, thereby enabling the formation of well-ordered CC structures. Moreover, the reflection colors of CC films could be easily tuned by controlling the molecular weight of POA chains grafted on the SiP surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.