Abstract
AbstractThis study deals with the cold compaction of polyether‐etherketone (PEEK) and nickel powder blends. Four different types of PEEK powders which are commercially available from Imperial Chemical Industries (ICI) were utilized for this investigation. These PEEK powders included fine and coarse size powders of a low viscosity grade (150PF and 150P) and similar powders of a high viscosity grade (450PF and 450P). Each of the four different PEEK powders were blended with about 10 vol−% nickel powder (Novamet) using a dry mixing technique. These PEEK/nickel powder blends were then successfully compacted at room temperature. Green strengths as high as 39.5 MPa and 26.3 MPa were measured on nickel filled 150 grade and 450 grade compacts, respectively. The higher strength values of the nickel filled compacts compared to their respective unfilled ones were attributed to a higher degree of mechanical interlocking and plastic deformation, which was induced in the polymer particles during compaction by the hard nickel filler. These composites also exhibited lower viscoelastic recoveries than their respective unfilled compacts. Electrical resistivities as low as 0.06 ohm‐cm were achieved by compacting 150P/nickel powder blends. This resistivity value agreed well with the calculated value predicted from the literature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.