Abstract
In this work, we report on the growth of (001) β-(AlxGa1−x)2O3 films in molecular beam epitaxy via metal oxide-catalyzed epitaxy. Films with Al contents up to 15% were grown and the Al content was measured with atom probe tomography. A relationship between the Al content and the out-of-plane lattice parameter was derived for both (001) and (100) orientations. Transmission electron microscopy showed no evidence of extended defects in (001) β-(AlxGa1−x)2O3, and reciprocal space maps confirmed that β-(AlxGa1−x)2O3 films were coherently strained to (001) β-Ga2O3. Sn was also demonstrated to act as a surfactant for (001) β-(AlxGa1−x)2O3 growth, allowing for high-quality, uniform films with smooth morphologies.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.