Abstract
AbstractThe overall crystallization rates of poly (3‐hexyl thiophene) (P3HT) cocrystals with different amount of regioregularity of the components are measured using differential scanning calorimetry (DSC). Two pairs of cocrystals with varying compositions of the component polymers (viz P3HT(R) (regioregularity 92 mol %)/P3HT‐2 (regioregularity 82 mol %), and P3HT‐2/P3HT‐1 (regioregularity 75 mol %)) are used. The crystallization rate at the same isothermal crystallization temperature (Tc) decreases with increasing regioregularity. The low Avrami exponent values (0.15–1.0) in all the samples suggest the presence of rigid amorphous portion, which cannot diffuse out quickly from the crystal growth front (soft impingement). Analysis of crystallization rate using Laurintzen–Hoffman (L–H) growth rate theory indicates Regime I to Regime II transition in all the samples. The product of lateral and end surface energy values (σσe) increases gradually with increasing regioirregularity in the blend. Analysis of σ values indicates chain extension of the components in the melt of the blend and the entropy of activation (ΔSI–II) of the cocrystals are higher than those of the components. The entropy of cocrystallization (ΔSc) values are 1–2.4 e.u for P3HT(R)/P3HT‐2 system and 0.5–1 e.u for P3HT‐2/P3HT‐1 system. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3811–3820, 2006
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.