Abstract
An electrochemical sensor based on a cobalt oxide nanorod (Co3O4NR) modified glassy carbon electrode (GCE) (Co3O4NR-GCE) was prepared for simultaneous and selective determination of hydroquinone (HQ) and catechol (CT). Surface morphology and crystallinity of Co3O4NR were investigated employing field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) analysis. The structure (16 nm) of the Co3O4 nanorod was observed in the FESEM image. A sharp peak pattern in the XRD survey revealed the following crystal planes in Co3O4NR material: (111), (220), (311), (222), (400), (422), (511), and (440). Electrochemical characterization of modified Co3O4NR-GCE was carried out performing cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). Selective and simultaneous detection of HQ and CT was carried out by performing CV and differential pulse voltammetry (DPV) analysis. In both studies, modified Co3O4NR-GCE showed well defined oxidation and reduction peaks for HQ and CT with enhanced peak current, and the oxidation peaks for HQ and CT were observed at 0.152 V and 0.254 V, respectively, in the CV analysis. Scan rate and pH variation analysis were performed to evaluate different kinetic parameters, including charge transfer coefficient (α = 0.56 for HQ and 0.66 for CT), heterogeneous charge transfer rate constant (ks = 56 for HQ and 72 for CT), and the number of electrons involved in HQ and CT oxidation. Quantitative analysis of HQ and CT was studied by observing the current response of DPV analysis with respect to concentration variation. Here, the detection limit was calculated as 0.2 µM for HQ with a linear concentration range of 5–200 µM, and 0.4 µM for CT with a linear concentration range of 5–150 µM. The practical applicability of the proposed sensor was investigated using sample solutions prepared in tap water. The reported sensor showed impressive selectivity towards HQ and CT in the presence of common interferents.
Highlights
The surface morphology and crystallinity of the Co3O4NR were investigated by field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) analysis
This study further indicated improved electrocatalytic properties of the Co3 O4 NR-glassy carbon electrode (GCE) surface for the oxidation of HQ and CT
The proposed Co3 O4 NR-GCE sensor can effectively resolve the redox peak of HQ
Summary
Industrialization often has negative consequences on the environment. Industrial byproducts and toxic chemicals can cause environmental pollution and degradation of creativecommons.org/licenses/by/. Among different transition metal oxides, Co3 O4 has been exploited as a potential sensing material due to its unique characteristics such as high surface area, high electrocatalytic activity, long term performance stability, and simple preparation method [28]. It is a p-type semiconductor containing cobalt ions in two oxidation states, namely Co2+ in tetrahedral and Co3+ in octahedral sites [29]. Practical applicability of the reported sensor was evaluated by using tap water as a real sample
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.