Abstract
The precursors with NiCO3 · 2Ni(OH)2 · 2H2O, Fe2O3 · nH2O coated alumina microspheres were prepared by the aqueous heterogeneous precipitation using metal salts, ammonium bicarbonate and α-Al2O3 micropowders as the starting materials. Magnetic metal Ni, α-Fe coated alumina, core-shell structural microspheres were successfully obtained by thermal reduction of the precursors at 700 °C for 2 h, respectively. Powders of the precursors and the resultant metal (Ni, α-Fe) coated alumina micropowders were characterized by scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction. The results show that optimized precipitation parameters are concentration of alumina micropowders of 15 g/L, rate of adding reactants of 5 mL/min and pH value of 7.5. And under the optimized conditions, the spherical precursors without aggregations or agglomerations are obtained, then transferred into Ni, α-Fe coated alumina microspheres by thermal reduction. It is possible to adjust metal coating thicknesses and fabricate a multilayer structured metal/ceramics, core-shell microspherical powder materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.