By using the hard template method, CMK-3 can be synthesized. The large Brunauer–Emmett–Teller surface area and total pore volume of CMK-3 were 1134 m2/g and 1.128 cm3/g, respectively. The sorption isotherms of CO2 on CMK-3 in the presence of MDEA solutions were measured. It was shown that the CO2 sorption capacity at low pressure was enhanced by chemical absorption and was higher than that of CMK-3 in the presence of water. However, the formation of the CO2 hydrate was inhibited. When the concentration of the MDEA solution exceeded 1.4 mol/L, no hydrate was formed, and the sorption capacity was only 13 mmol/g at approximately 3.5 MPa, which was significantly lower than that of the water under the same pressure. The inhibitory effect of MDEA on hydrate formation was reduced at a low solution concentration. When the concentration of the MDEA solution was 0.52 mol/L, the gas hydrate was formed at approximately 1.88 MPa; the sorption capacity was approximately 28.7 mmol/g at 3.58 MPa, which was close to the h...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.