Abstract
The reaction of Co with epitaxial SiGeC/Si layers is investigated and compared to the reaction of Co with SiGe/Si layers. The sequence of phase formation is the same as the reaction of Co with monocrystalline Si, however, cobalt disilicide is formed at much higher temperatures. The presence of C further delays the disilicide formation, as a result of C accumulation at the silicide/substrate interface during the reaction, which blocks the Co diffusion paths. The CoSi2 layers thus formed exhibit a preferential (h00) orientation. The slow supply of Co atoms to the silicide/Si interface, due to the blocking of Co diffusion paths by Ge and C, is believed to be the reason for this epitaxial alignment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.