Abstract
Strontium Bismuth Niobate (SrBi2Nb2O9) was synthesized by co-precipitation-hydrothermal method. Precipitation step was first carried out at room temperature at which the powder was prepared from aqueous solution of Bi(NO3)3, Sr(NO3)2 and Nb2O5. Then the process is completed by hydrothermal treatment. The compound crystallized in the orthorhombic structure. The characteristic bands, at approximately 619cm−1 and 816cm−1 were observed. The grain size is around 1µm. The dielectric properties at room temperature show low loss values at higher frequencies which makes it suitable for ferroelectric random access memory applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.