Co-60 gamma radiation assisted diffusion of iodine in polypropylene

Abstract

Thin films of polypropylene having dimensions 50 mm × 15 mm × 350 μm were immersed in 1 N iodine solution and then irradiated with Co-60 gamma radiation for the periods of 48, 96 and 144 h at the doses varying from 14.4 to 43.2 kGy. The films were also kept immersed in iodine solution for similar periods but without irradiation. Furthermore, the films were also directly-irradiated with Co-60 gamma radiation for similar periods and doses. The radiation-iodinated, plain-iodinated and directly-irradiated samples were characterized by using various techniques such as weight gain EDS, SEM, FTIR, UV–visible spectroscopy, contact angle and XRD. Weight gain, EDS and SEM collectively reveal that gamma irradiation enhances iodine intake in polypropylene. FTIR, EDS and contact angle measurements indicate that presence of iodine during irradiation resists radiation induced carbonylation of polypropylene. FTIR also shows presence of HOI (Hypoiodous acid) species instead of expected C–I bonds. UV–visible analysis unambiguously shows that presence of iodine enhances radiation induced band gap reduction process of polypropylene. XRD indicates that iodine decreases the crystallinity of polypropylene.