Abstract
Submicrometer silicon photodiode waveguides, fabricated on silicon-on-insulator substrates, have photoresponse from <1270 to 1740 nm (0.8 AW <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> at 1550 nm) and a 3-dB bandwidth of 10 to 20 GHz. The p-i-n photodiode waveguide consists of an intrinsic waveguide 500times250 nm where the optical mode is confined and two thin, 50-nm-thick, doped Si wings that extend 5 mum out from either side of the waveguide. The Si wings, which are doped one p-type and the other n-type, make electric contact to the waveguide with minimal effect on the optical mode. The edges of the wings are metalized to increase electrical conductivity. Ion implantation of Si <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> 1times10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">13</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> at 190 keV into the waveguide increases the optical absorption from 2-3 dBmiddotcm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> to 200-100 dBmiddotcm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> and causes the generation of a photocurrent when the waveguide is illuminated with subbandgap radiation. The diodes are not damaged by annealing to 450 degC for 15 s or 300 degC for 15 min. The photoresponse and thermal stability is believed due to an oxygen stabilized divacancy complex formed during ion implantation
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.